| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D1505 | 0.956 g/cm³ |
| melt mass-flow rate | 190°C/2.16 kg | ASTM D1238 | 0.040 g/10 min |
| Environmental stress cracking resistance | 25% Igepal, F50 | ASTM D1693B | > 1000 hr |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏 D | ASTM D2240 | 64 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服 | ASTM D638 | 29.4 Mpa |
| tensile strength | 断裂 | ASTM D638 | 38.2 Mpa |
| elongation | 断裂 | ASTM D638 | 820 % |
| Flexural modulus | | ASTM D747 | 932 Mpa |
| Flexural modulus | | ASTM D790 | 1180 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 290 J/m |
| squeeze out | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Temperature in Zone 1 of the material cylinder | | | 180 to 200 °C |
| Temperature in Zone 3 of the material cylinder | | | 180 to 200 °C |
| Temperature in Zone 5 of the material cylinder | | | 180 to 200 °C |
| die temperature | | | 190 to 210 °C |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| vicat | | ASTM D15253 | 125 °C |
| melting temperature | | ASTM D3418 | 125 °C |