flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.6mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.5mm	UL 94	V-0
Burning wire flammability index	2.0mm	IEC 60695-2-12	960	°C
Ignition temperature of heating wire	2.0mm	IEC 60695-2-13	800	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	4.00mm,Injection	ISO 527-2/1	2600	Mpa
tensile strength	Yield,4.00mm,InjectionMolded	ISO 527-2/50	60.0	Mpa
tensile strength	tensile strength	Break,4.00mm,Injection	ISO 527-2/50	47.0	Mpa
Tensile strain	Yield,4.00mm,InjectionMolded	ISO 527-2/50	4.0	%
Tensile strain	Tensile strain	Break,4.00mm,Injection	ISO 527-2/50	40	%
Bending modulus	4.00mm,InjectionMolded	ISO 178	2700	Mpa
bending strength	4.00mm,InjectionMolded	ISO 178	92.0	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	80.0	°C
Vicat softening temperature	--	ISO 306/A120	105	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	98.0	°C
Ball pressure temperature		IEC 60335-1	95.0	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	90.0	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Apparent density		ISO 60	0.67	g/cm³
melt mass-flow rate	230°C/3.8kg	ISO 1133	20	g/10min
melt mass-flow rate	melt mass-flow rate	260°C/5.0kg	ISO 1133	95	g/10min
Shrinkage rate	MD	ISO 294-4	0.40-0.60	%

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.