ASA+PA SCHULABLEND® (ASA/PA) M/MW NC 800
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| Flammability level | 1.5mm | IEC 60695-11-10,-20 | HB |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 5.0 kJ/m² |
| 23°C | ISO 179/1eA | 9.0 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 79.0 MPa |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 97.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 70.0 °C | |
| vicat | ISO 306/B50 | 139 °C | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| Tensile strain | Yield | ISO 527-2/1A/50 | 3.0 % |
| density | ISO 1183/A | 1.16 g/cm³ | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 18.0 cm³/10min |
| Tensile modulus | ISO 527-2/1A/1 | 3400 MPa | |
| tensile strength | Yield | ISO 527-2/1A/50 | 57.0 MPa |