| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 15.0 cm3/10min |
| Shrinkage rate | MD1 | 内部方法 | 0.40-0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 118 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 104 Mpa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.750mm | UL 94 | HB |
| UL flame retardant rating | 3.00mm | UL 94 | HB |
| Burning wire flammability index | 3.20mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 20 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 45 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| yield | | ISO 527-2/50 | 59.0 Mpa |
| fracture | | ISO 527-2/5 | 55.0 Mpa |
| fracture | | ISO 527-2/50 | 59.0 Mpa |
| yield | | ISO 527-2/5 | 4.0 % |
| fracture | | ISO 527-2/5 | 120 % |
| fracture | | ISO 527-2/50 | >50 % |
| Flexural modulus | | ISO 178 | 2400 Mpa |
| bending strength | | ISO 178 | 80.0 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 125 mg |
| Tensile modulus | | ISO 527-2/1 | 2500 Mpa |
| yield | | ISO 527-2/5 | 55.0 Mpa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | >1.0E+15 ohms |
| Volume resistivity | | IEC 60093 | >1.0E+15 ohms·cm |
| dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| 0.45MPa, Unanealed, 100mm span | | ISO 75-2/Be | 125 °C |
| 1.8MPa, Unanealed, 100mm span | | ISO 75-2/Ae | 101 °C |
| ball-indentation hardness | 75°C | IEC 60695-10-2 | Pass |
| ball-indentation hardness | 105°C7 | IEC 60695-10-2 | Pass |
| Linear coefficient of thermal expansion | MD：23到60°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| thermal conductivity | | ISO 8302 | 0.20 W/m/K |
| RTI Elec | | UL 746 | 50.0 °C |
| RTI Imp | | UL 746 | 50.0 °C |
| RTI | | UL 746 | 50.0 °C |