impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	70	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.40mm	UL 94	V-0
	UL flame retardant rating	0.8mm	UL 94	V-0
		UL flame retardant rating	1.6mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	3.2mm	UL 94	V-0
Burning wire flammability index	0.8mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	1.6mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	Burning wire flammability index	3.2mm	IEC 60695-2-12	960	°C
Ignition temperature of heating wire	1.6mm	IEC 60695-2-13	650	°C
Extreme Oxygen Index		ISO 4589-2	33	%
UL flame retardant rating		NFF16-101	F2
smoke density		NFF16-101	I2
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of cantilever beam gap		ASTM D256/ISO 179	60	kg·cm/cm(J/M)ft·lb/in
Elongation at Break		ASTM D638/ISO 527	>50	%
Tensile modulus		ASTM D638/ISO 527	3700	kg/cm²(MPa)[Lb/in²]
tensile strength		ASTM D638/ISO 527	80	kg/cm²(MPa)[Lb/in²]
Tensile modulus	23°C	ISO 527-2/1A	3750	Mpa
tensile strength	Yield,23°C	ASTM D638	85.0	Mpa
	tensile strength	Yield,23°C	ISO 527-2/1A	80.0	Mpa
	tensile strength	tensile strength	Break,23°C	ISO 527-2/1A	70.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.0	%
elongation	Break,23°C	ASTM D638	15	%
Tensile strain	Break,23°C	ISO 527-2	12	%
Bending modulus	23°C	ASTM D790	3800	Mpa
Bending modulus	Bending modulus	23°C	ISO 178	3700	Mpa
bending strength	23°C	ASTM D790	125	Mpa
bending strength	bending strength	23°C	ISO 178	130	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	HDT	ASTM D648/ISO 75	85	℃（℉）
Melting temperature			242	℃（℉）
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	6.5	mm/mm.℃
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	85.0	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/Af	85.0	°C
Melting temperature		ISO 11357-3	242	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D792/ISO 1183	1.16
Water absorption rate	23°C,24hr	ISO 62	1.1	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	3.1	%
Outdoor applicability		UL 746C	f1
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dielectric constant		ASTM D150/IEC 60250	34
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 0
Surface resistivity		IEC 60093	1E+15	ohms
Volume resistivity		IEC 60093	1E+15	ohms·cm
Dielectric strength	0.800mm	IEC 60243-1	33	KV/mm
Relative permittivity		IEC 60250	3.60
Dissipation factor		IEC 60250	0.020
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
EuropeanRailwaysCertifications	R22	EN45545-2	HL2
EuropeanRailwaysCertifications	EuropeanRailwaysCertifications	R23	EN45545-2	HL3