برگه داده فنی
physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
transmittance | ASTM D-1003 | 92 % | |
Shrinkage rate | (冷模/冷件),48hrs | ASTM D-935 | 0.3-0.6 % |
refractive index | ASTM D-542 | 1.49 | |
density | ASTM D-792 | 1.17 |
Basic performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Water absorption rate | 浸水24hrs后增重 | ASTM D-570 | 0.3 % |
melt mass-flow rate | ASTM D-1238 | 3.2 g/10min |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Impact strength of cantilever beam gap | Izod研磨缺口 | ASTM D-256 | 3.2(31.4) kgf.cm/cm(J/m) |
tensile strength | 初级应变速率0.1cm/cm/min | ASTM D-638 | 490(48) kgf/cm |
Flexural modulus | ASTM D-790 | 27000 kgf/cm | |
bending strength | 横跨比=16 | ASTM D-790 | 1010(99) kgf/cm |
Impact strength of cantilever beam gap | 落锤(15.2×15.2×0.3cm重1.4kg半径0.64cm) | ASTM D-256 | 95(10) kg.cm(J) |
Rockwell hardness | ASTM D-758 | 68 M scale |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|---|---|---|
Temperature range for use | 与残余应力大小有关 | 85 ℃ | |
vicat | 未退火,50℃/hr,1kg | ASTM D-1525 | 99 ℃ |
Heat distortion temperature | 退火2℃/min,18.6kgf/cm,HDT | ASTM D-648 | 85 ℃ |
vicat | 未退火,50℃/hr,5kg | ASTM D-1525 | 90 ℃ |
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.