PA6 Nycast CP Cast Nylons Ltd.

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap		ASTM D256	48to75 J/m

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus		ASTM D638	1650to2280 MPa
tensile strength		ASTM D638	60.0to79.3 MPa
elongation	Break	ASTM D638	25to80 %
Bending modulus		ASTM D790	1970to2650 MPa
bending strength		ASTM D790	103to138 MPa
Compressive modulus		ASTM D695	1380to2070 MPa
compressive strength		ASTM D695	75.8to86.2 MPa
shear strength		ASTM D732	52.4to62.1 MPa
Friction coefficient	Itself - Dynamic	ASTM D1894	0.22
Hot deformation temperature	HDT	ASTM D621	0.400to0.700 %

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Linear coefficient of thermal expansion	MD	ASTM D696	9E-05 cm/cm/°C
Usage temperature	间歇		149 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	204to221 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	93.3to204 °C
Continuous use temperature		ASTM D794	98.9 °C
Melting temperature			204to216 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Water absorption rate	Saturation	ASTM D570	4.0to5.0 %
density		ASTM D792	1.10to1.13 g/cm³
Water absorption rate	24hr	ASTM D570	0.50to0.60 %

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dielectric strength		ASTM D149	20to24 kV/mm
Dielectric constant	60Hz	ASTM D150	3.70
	Dielectric constant	1kHz	ASTM D150	3.70
	Dielectric constant	Dielectric constant	100kHz	ASTM D150	3.70

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Scale	ASTM D785	100to115
Shore hardness	ShoreD	ASTM D2240	75to81

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.