برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.19 g/cm³ |
| Water absorption rate | 23°C,24hr,0.250mm | ASTM D570 | 0.50 % |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | 60°,250µm | ASTM D2457 | 161 |
| refractive index | | ASTM D542 | 1.550 |
| transmissivity | 250µm | ASTM D1003 | 92.0 % |
| Haze ratio | 250µm | ASTM D1003 | 0.70 % |
| Yellowness Index | 250mm | ASTM D1925 | 0.50 YI |
| UV Transmittance | 250.0µm | | 89 % |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| SurfaceEnergy | Total:23°C,250.0µm | ASTM D5946 | 46 dyne/cm |
| SurfaceEnergy | Dispersive:23°C,250.0µm | ASTM D5946 | 39 dyne/cm |
| SurfaceEnergy | Polar:23°C,250mm | ASTM D5946 | 8 dyne/cm |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Abrasion | 23°C | ASTM D1044 | 23haze % |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tear strength | 开裂8 | ASTM D1938 | 12 kN/m |
| tear strength | 开裂9 | ASTM D1938 | 13 kN/m |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | TD:屈服,250µm | ASTM D882 | 40.0 MPa |
| tensile strength | MD:断裂,250µm | ASTM D882 | 59.0 MPa |
| tensile strength | TD:断裂,250µm | ASTM D882 | 52.0 MPa |
| elongation | MD:屈服,250µm | ASTM D882 | 7.0 % |
| elongation | TD:屈服,250µm | ASTM D882 | 7.0 % |
| elongation | MD:断裂,250µm | ASTM D882 | 180 % |
| Water Vapor Transmission Rate | 23°C,100%RH,250µm | ASTMF1249 | 4.0 g/m²/24hr |
| Water Vapor Transmission Rate | 38°C,100%RH,250µm | ASTMF1249 | 11 g/m²/24hr |
| Carbon dioxide transmittance | 23°C,254.0µm | ASTM D1434 | 150 cm³·mm/m²/atm/24hr |
| Elmendorf tear strength | MD:23°C,250.0µm | ASTM D1922 | 5 N |
| Elmendorf tear strength | TD:23°C,250.0µm | | 6 N |
| PPTTearResistance | MD:23°C,250.0µm | ASTM D2582 | 42 N |
| PPTTearResistance | TD:23°C,250.0µm | ASTM D2582 | 56 N |
| tear strength | MD:23°C,250.0µm | ASTM D1938 | 410 gf |
| tear strength | TD:23°C,250.0µm | ASTM D1938 | 310 gf |
| film thickness | | | 250 µm |
| Thin film puncture strength | 250µm | ASTM D3763 | 4.60 J |
| Secant modulus | MD:250µm | ASTM D882 | 1500 MPa |
| Secant modulus | TD:250µm | ASTM D882 | 1400 MPa |
| tensile strength | MD:屈服,250µm | ASTM D882 | 41.0 MPa |
| Tear resistance of pants | TD:250µm | ISO 6383-1 | 11.0 N/mm |
| OTr | 23°C,250µm,50%RH | ASTM D3985 | 32 cm³·mm/m²/atm/24hr |
| elongation | TD:断裂 | ASTM D882 | 200 % |
| Dart impact | -30°C,250µm | ASTM D1709A | 910 g |
| Dart impact | 23°C,250µm | ASTM D1709A | 880 g |
| Tear resistance of pants | MD:250µm | ISO 6383-1 | 11.0 N/mm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| specific heat | 60°C | DSC | 1700 J/kg/°C |
| specific heat | 100°C | DSC | 1900 J/kg/°C |
| specific heat | 150°C | DSC | 2200 J/kg/°C |
| specific heat | 200°C | DSC | 2400 J/kg/°C |
| specific heat | 250°C | DSC | 2600 J/kg/°C |
| melting temperature | | | 110 °C |
| Linear coefficient of thermal expansion | MD：23°C,0.250mm | ASTM D696 | 9E-05 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.