PA66/6 C70 FR HF Bada AG

کاربردها:
Electrical components
مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23℃	kJ/m²	0.556to4.643
Impact strength of simply supported beam without notch	23℃	kJ/m²	10.679to23.215
Impact strength of cantilever beam gap	23℃	kJ/m²	1.988to6.176

flammability	روش آزمون	نتیجه آزمون
Extreme Oxygen Index	%	21to28
Burning wire flammability index	°C	954to960
Hot filament ignition temperature	°C	743to960

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
crack			40.0to171.72 Mpa
crack	crack		%	3,0到77
yield			39.03to89.66 Mpa
Friction coefficient			0.30-1.0
crack			79.31to84.83 Mpa
crack	crack		%	2,2到12
Nominal tensile fracture strain	23℃	%	5,6到50
Tensile modulus	23℃		477.24到0.01,0.04E0.05 Mpa
yield		%	3,0到21
yield	yield			64.76to85.52 Mpa

thermal performance	روش آزمون	نتیجه آزمون
flow	mm/mm/°C	99.1E-5-101.6E-5
Continuous use temperature	°C	87to202
flow	mm/mm/°C	96.5E-5-152.4E-5
transverse	mm/mm/°C	99.1E-5-203.2E-5
Vicat softening temperature	°C	67to247

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
saturated		%	7,9到11
Stickiness		cm³/g	138to247
balance		%	2.5
melt mass-flow rate	235°C/1.0kg	g/10min	1.2-5.0
flow		mm/mm	152.4E-3-0.635
balance		%	2.5-3.5
saturated		%	9.0
Apparent density		g/cm³	0.70-0.78

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Dissipation factor	23℃		0.020-0.30
Volume resistivity	相对电容率(23℃)		3.50
Surface resistivity		ohms	1.0E+2-2.5E+13
Compared to the anti leakage trace index		V	PLC 0

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Ball Pressure Test			45.03to201.38 Mpa
Shore hardness	23℃		77to80