ASA+PA SCHULABLEND® (ASA/PA) M/MW NC 100 SF K2083 A SCHULMAN USA
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| bending strength | ISO 178 | 75.6 MPa | |
| Bending Strain | ISO 178 | 5.1 % | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 38 kJ/m² |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 106 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 70.0 °C | |
| vicat | ISO 306/B50 | 120 °C | |
| burning rate | ISO 3795 | <60 mm/min | |
| Flexural modulus | ISO 178 | 3000 MPa | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 20.3 cm³/10min |
| Tensile modulus | ISO 527-2/1A/1 | 3240 MPa | |
| tensile strength | Yield | ISO 527-2/1A/50 | 50.5 MPa |
| Break | ISO 527-2/1A/50 | 48.0 MPa | |
| Tensile strain | Yield | ISO 527-2/1A/50 | 2.8 % |
| Nominal tensile fracture strain | ISO 527-2/1A/50 | 25 % | |
| density | ISO 1183/A | 1.17 g/cm³ |