ASA+PA SCHULABLEND® (ASA/PA) M/MW 6201 MT
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 78.0 °C |
| vicat | -- | ISO 306/A50 | 184 °C |
| -- | ISO 306/B50 | 110 °C | |
| burning rate | ISO 3795 | 30 mm/min | |
| UL flame retardant rating | 1.5mm | IEC 60695-11-10,-20 | HB |
| density | ISO 1183/A | 1.18 g/cm³ | |
| Melt volume flow rate | 250°C/5.0kg | ISO 1133 | 6.00 cm³/10min |
| Tensile modulus | ISO 527-2/1A/1 | 3100 MPa | |
| tensile strength | Yield | ISO 527-2/1A/50 | 51.0 MPa |
| Tensile strain | Yield | ISO 527-2/1A/50 | 3.1 % |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| UL flame retardant rating | 3.0mm | IEC 60695-11-10,-20 | HB |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 675 °C |
| 3.0mm | IEC 60695-2-12 | 675 °C | |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 700 °C |
| 3.0mm | IEC 60695-2-13 | 700 °C | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 75 kJ/m² |
| 23°C | ISO 179/1eU | NoBreak | |
| ball-indentation hardness | H358/10 | ISO 2039-1 | 101 MPa |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 96.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.