برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.04 g/cm³ |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.30 % |
| density | | ISO 1183 | 1.04 g/cm³ |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 15 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.40-0.60 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R级 | ASTM D785 | 105 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | | ISO 527-2/1 | 2100 Mpa |
| tensile strength | 屈服 | ASTM D638 | 41.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | >10 % |
| Flexural modulus | | ASTM D790 | 1960 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 44.0 Mpa |
| elongation | 断裂 | ASTM D638 | 40 % |
| bending strength | | ISO 178 | 63.0 Mpa |
| bending strength | | ASTM D790 | 63.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C,12.7mm | ASTM D256 | 290 J/m |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 310 J/m |
| Impact strength of cantilever beam gap | -30°C,12.7mm | ASTM D256 | 140 J/m |
| Impact strength of cantilever beam gap | 0°C,3.20mm | ASTM D256 | 230 J/m |
| Impact strength of cantilever beam gap | 0°C,12.7mm | ASTM D256 | 200 J/m |
| Impact strength of cantilever beam gap | -30°C,3.20mm | ASTM D256 | 160 J/m |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 26 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 1kHz | ASTM D150 | 6.5E-03 |
| dielectric strength | | ASTM D149 | 24 KV/mm |
| dielectric constant | 1kHz | ASTM D150 | 3.10 |
| Surface Resistivity | | ASTM D257 | >1.0E+16 ohms |
| Volume resistivity | 23°C | ASTM D257 | >1.0E+16 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| thermal conductivity | | ASTMC177 | 0.15 W/m/K |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7.6E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,12.7mm，HDT | ASTM D648 | 91.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 85.0 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.