برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.70to1.80 g/cm³ |
| Apparent density | | ISO 60 | 0.75to0.95 g/cm³ |
| Shrinkage rate | MD1 | ISO 2577 | 0.70to1.0 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.80 % |
| Shrinkage rate | | ISO 2577 | 0.20to0.40 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.750mm | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 825 °C |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compression molding temperature | | | 160to180 °C |
| Compression molding pressure | | | >10.0 MPa |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Flexural modulus | Injection | ISO 178 | 9000to11000 MPa |
| bending strength | Compression Molded | ISO 178 | 60.0to90.0 MPa |
| bending strength | Injection | ISO 178 | 90.0to110 MPa |
| compression stress | | ISO 604 | 150to200 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 5000to7000 MPa |
| Tensile modulus | Injection | ISO 527-2 | 9000to10000 MPa |
| tensile strength | CompressionMolded | ISO 527-2 | 30.0to50.0 MPa |
| tensile strength | InjectionMolded | ISO 527-2 | 45.0to55.0 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 6000to8000 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 1.5to2.5 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 2.0to3.0 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 6.0to8.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 9.0to11 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 1MHz | IEC 60250 | 0.030to0.050 |
| arc resistance | | ASTM D495 | PLC 4 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Surface Resistivity | | IEC 60093 | 1.0E+12到1.0E+13 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+13到1.0E+14 ohms·cm |
| dielectric strength | | IEC 60243-1 | 30to40 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 7.005.00 |
| relative permittivity | 1MHz | IEC 60250 | 5.004.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.10to0.20 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 2.0E-5到3.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.60to0.70 W/m/K |
| maximum service temperature | <50h | IEC 60216 | 190 °C |
| maximum service temperature | 20,000h | IEC 60216 | 140 °C |