PC+PBT Makroblend® UT3907 Covestro - Polycarbonates
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shrinkage rate | TD:90°C,1hr | ISO 2577 | 0.10to0.20 % |
| MD2 | ISO 2577 | 0.70to0.90 % | |
| MD:90°C,1hr | ISO 2577 | 0.10to0.20 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % | |
| density | 23°C | ISO 1183 | 1.20 g/cm³ |
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 44.0 cm³/10min |
| Shrinkage rate | TD2 | ISO 2577 | 0.70to0.90 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 107 MPa |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 750 °C |
| Limiting Oxygen Index | ISO 4589-2 | 21 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Bending Strain | 23°C | ISO 178 | 6.0 % |
| Flexural modulus | 23°C | ISO 178 | 2150 MPa |
| bending strength | 23°C | ISO 178 | 80.0 MPa |
| 3.5%Strain,23°C | ISO 178 | 70.0 MPa | |
| Tensile modulus | 23°C | ISO 527-2/1 | 2200 MPa |
| tensile strength | 屈服,23°C | ISO 527-2/50 | 60.0 MPa |
| 断裂,23°C | ISO 527-2/50 | 50.0 MPa | |
| Tensile strain | 屈服,23°C | ISO 527-2/50 | 5.0 % |
| Nominal tensile fracture strain | 23°C | ISO 527-2/50 | >100 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 25 kJ/m² |
| 23°C | ISO 179/1eA | 55 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/A | 20 kJ/m² |
| -30°C | ISO 180/A | 25 kJ/m² | |
| -20°C | ISO 180/A | 35 kJ/m² | |
| 23°C | ISO 180/A | 40 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180 | NoBreak |
| 23°C | ISO 180 | NoBreak | |
| Multi axis Instrumented Impact Energy | -30°C | ISO 6603-2 | 55.0 J |
| 23°C | ISO 6603-2 | 45.0 J | |
| Multi axis Instrumented Peak Impact Force | -30°C | ISO 6603-2 | 4800 N |
| 23°C | ISO 6603-2 | 3600 N |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+17 ohms | |
| Volume resistivity | 23°C | IEC 60093 | >1.0E+17 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 30 kV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 3.20 |
| 23°C,1MHz | IEC 60250 | 3.00 | |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 6E-04 |
| 23°C,1MHz | IEC 60250 | 4.5E-03 | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| 解决方案B | IEC 60112 | PLC 4 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 105 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 82.0 °C | |
| vicat | ISO 306/B120 | 122 °C | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 9E-05 cm/cm/°C |
| TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| thermal conductivity | 23°C | ISO 8302 | 0.20 W/m/K |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.