برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ISO 1183 | 1.65to1.80 g/cm³ |
| Apparent density | | ISO 60 | 0.60to0.80 g/cm³ |
| Shrinkage rate | MD2 | ISO 2577 | 0.30to0.50 % |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.20 % |
| Shrinkage rate | | ISO 2577 | <0.20 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | | IEC 60695-2-13 | 960 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | Injection | ISO 527-2 | 6000to9000 MPa |
| tensile strength | CompressionMolded | ISO 527-2 | 70.0to90.0 MPa |
| tensile strength | Injection | ISO 527-2 | 90.0to110 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 11000to13000 MPa |
| Flexural modulus | Injection | ISO 178 | 12000to14000 MPa |
| bending strength | Compression Molded | ISO 178 | 110to140 MPa |
| bending strength | Injection | ISO 178 | 150to180 MPa |
| compression stress | | ISO 604 | 250to300 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 6000to9000 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | Compression Molded | ISO 179/1eU | 7.0to10 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO 179/1eU | 13to17 kJ/m² |
| Charpy Notched Impact Strength | Injection | ISO 179/1eA | 3.0to5.0 kJ/m² |
| Charpy Notched Impact Strength | Compression Molded | ISO 179/1eA | 2.0to4.0 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| Surface Resistivity | | IEC 60093 | 1.0E+10到1.0E+11 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+12到1.0E+13 ohms·cm |
| dielectric strength | | IEC 60243-1 | 20to30 kV/mm |
| relative permittivity | 100Hz | IEC 60250 | 6.008.00 |
| relative permittivity | 1MHz | IEC 60250 | 4.006.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010to0.020 |
| Dissipation Factor | 1MHz | IEC 60250 | 0.020to0.030 |
| arc resistance | | ASTM D495 | PLC 4 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：50到150°C | ISO 11359-2 | 1.4E-5到1.6E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.40to0.60 W/m/K |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | >200 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | >170 °C |