PP EnCom T CPP 2005

0

برگه داده فنی

physical property شرایط آزمونروش آزموننتیجه آزمون
densityASTM D7921.08 g/cm³
melt mass-flow rate230°C/2.16kgASTM D12387.5 g/10min
densityASTM D7921.08 g/cm³
melt mass-flow rate230°C/2.16kgASTM D12387.5 g/10min
Shrinkage rateMD:3.18mmASTM D9550.10 %
Shrinkage rateMD:3.18mmASTM D9550.10 %
Mechanical propertiesشرایط آزمونروش آزموننتیجه آزمون
elongationBreakASTM D63822 %
Flexural modulusASTM D7901640 MPa
bending strengthYieldASTM D79033.8 MPa
tensile strength YieldASTM D63822.1 MPa
elongationBreakASTM D63822 %
Flexural modulusASTM D7901640 MPa
bending strengthYieldASTM D79033.8 MPa
tensile strength YieldASTM D63822.1 MPa
Impact resistanceشرایط آزمونروش آزموننتیجه آزمون
Impact strength of cantilever beam gap23°CASTM D256880 J/m
Dart impactASTM D302923.2 J
Impact strength of cantilever beam gap23°CASTM D256130 J/m
Impact strength of cantilever beam gap23°CASTM D256130 J/m
Impact strength of cantilever beam gap23°CASTM D256880 J/m
Dart impactASTM D302923.2 J
Thermal performanceشرایط آزمونروش آزموننتیجه آزمون
Heat distortion temperature0.45MPa,未退火,HDTASTM D648117 °C
Heat distortion temperature0.45MPa,未退火,HDTASTM D648117 °C
Heat distortion temperature1.8MPa,未退火,HDTASTM D64862.2 °C
Heat distortion temperature1.8MPa,未退火,HDTASTM D64862.2 °C