POM M90CF2001 CELANESE NANJING

فرم：گرانول | درجه：درجه تزریق

تأمین‌کننده(1)

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	180	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	190	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.7	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	6.0	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2/1A/1	2760	Mpa
tensile strength	Yield,-40°C	ASTM D638	94.5	Mpa
	tensile strength	Yield,23°C	ASTM D638	60.7	Mpa
		tensile strength	Yield,71°C	ASTM D638	34.5	Mpa
		tensile strength	tensile strength	Yield	ISO 527-2/1A/50	65.0	Mpa
Tensile strain	Yield	ISO 527-2/1A/50	10	%
Tensile creep modulus	1hr	ISO 899-1	2450	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1350	Mpa
Bending modulus	23°C	ISO 178	2550	Mpa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Linear coefficient of thermal expansion	TD	ISO 11359-2	1.2E-04	cm/cm/°C
Effective thermal diffusivity coefficient		Internal Method	0.0485	cSt
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	158	°C
	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	110	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	101	°C
Melting temperature		ASTM D3418	165	°C
Melting temperature	Melting temperature		ISO 11357-3	165	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	1.2E-04	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ASTM D792	1.41	g/cm³
density	density		ISO 1183	1.41	g/cm³
melt mass-flow rate		ASTM D1238	9.0	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	8.00	cm3/10min
Shrinkage rate	MD	ASTM D955	2.2	%
	Shrinkage rate	TD	ASTM D955	1.8	%
		Shrinkage rate	TD	ISO 294-4	1.9	%
		Shrinkage rate	Shrinkage rate	MD	ISO 294-4	2.0	%
Water absorption rate	Saturation,23°C	ISO 62	0.75	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Density of Melt		Internal Method	1.200	g/cm³
SpecificHeatCapacity of Melt		Internal Method	2210	J/kg/°C
ThermalConductivityofMelt		Internal Method	0.16	W/m/K
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	3E+16	ohms
Volume resistivity		ASTM D257	1E+14	ohms·cm
Volume resistivity	Volume resistivity		IEC 60093	8E+14	ohms·cm

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.