optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
gloss	60°, 无织构	ASTM D523	30
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dart impact	-30°C, Total Energy	ASTM D3763	33.0	J
Dart impact	Dart impact	23°C, Total Energy	ASTM D3763	40.0	J
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Yield	ASTM D638	54.0	Mpa
elongation	Break	ASTM D638	75	%
Bending modulus	50.0 mm Span	ASTM D790	2300	Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	84.0	Mpa
injection	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
drying temperature			105 to 110	°C
drying time			3.0 to 4.0	hr
Suggested maximum moisture content			0.040	%
Suggested injection volume			30 to 80	%
Temperature at the rear of the barrel			250 to 290	°C
Temperature in the middle of the barrel			255 to 295	°C
Temperature at the front of the material cylinder			260 to 300	°C
Spray nozzle temperature			275 to 300	°C
Processing (melt) temperature			275 to 300	°C
Mold temperature			60 to 90	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			40 to 70	rpm
Exhaust hole depth			0.038 to 0.076	mm
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	123	°C
	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	129	°C
		Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	107	°C
		Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	110	°C
Vicat softening temperature		ASTM D15254	129	°C
Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	7.2E-5	cm/cm/°C
thermal conductivity		ASTM C177	0.20	W/m/K
RTI Elec		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
RTI		UL 746	60.0	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
melt mass-flow rate	260°C/5.0 kg	ASTM D1238	17	g/10 min
Shrinkage rate	Flow : 3.20 mm	Internal Method	0.50 - 0.70	%
Shrinkage rate	Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.50 - 0.70	%
Water absorption rate	24 hr	ASTM D570	0.10	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C	ASTM D570	0.40	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 2
High arc combustion index		UL 746	PLC 0
Hot wire ignition		UL 746	PLC 2
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	R-Scale	ASTM D785	118

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.