HMW-HDPE TOTAL Polyethylene HDPE 2287 TOTAL
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 0.950 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.080 g/10min |
| 190°C/21.6kg | ASTM D1238 | 11 g/10min | |
| 190°C/5.0kg | ASTM D1238 | 0.32 g/10min |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Dart impact | 20µm,吹塑薄膜 | ASTM D1709A | 350 g |
| Elmendorf tear strength | 20µm,BlownFilm，MD | ASTM D1922 | 24 g |
| 20µm,BlownFilm，TD | ASTM D1922 | 120 g | |
| Water Vapor Transmission Rate | ASTME96 | 12 g/m²/24hr | |
| film thickness | 20 µm | ||
| Secant modulus | 20µm,BlownFilm | ASTM D882A | 841 MPa |
| 20µm,BlownFilm | ASTM D882A | 910 MPa | |
| tensile strength | Yield,20µm,BlownFilm | ASTM D882A | 36.5 MPa |
| Yield,20µm,BlownFilm | ASTM D882A | 34.5 MPa | |
| Break,20µm,BlownFilm | ASTM D882A | 63.4 MPa | |
| Break,20µm,BlownFilm | ASTM D882A | 67.6 MPa | |
| Tensile strain | Break,20µm,BlownFilm，MD | ASTM D882A | 300to500 % |
| Break,20µm,BlownFilm | ASTM D882A | 300to500 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| melting temperature | ASTM D3417 | 127 °C |