| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.59 g/cm³ |
| Specific volume | | ASTM D792 | 0.640 cm³/g |
| Shrinkage rate | MD：--2 | 内部方法 | 0.50-0.80 % |
| Shrinkage rate | MD：--3 | 内部方法 | 0.30-0.50 % |
| Shrinkage rate | TD：--3 | 内部方法 | 0.40-0.60 % |
| Shrinkage rate | TD：--4 | 内部方法 | 0.60-0.90 % |
| Water absorption rate | 24hr | ASTM D570 | 0.070 % |
| Outdoor applicability | | UL 746C | f1 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.9mm | UL 94 | V-0 |
| UL flame retardant rating | 2.3mm | UL 94 | 5VA |
| Limiting Oxygen Index | | ASTM D2863 | 37 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | 640 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 85 J/m |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Break | ASTM D638 | 110 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 9400 Mpa |
| bending strength | Break,50.0mmSpan | ASTM D790 | 179 Mpa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 4.3E+16 ohms·cm |
| dielectric strength | 1.60mm,在油中 | ASTM D149 | 26 KV/mm |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| dielectric constant | 100Hz | ASTM D150 | 3.80 |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| Dissipation Factor | 100Hz | ASTM D150 | 2E-03 |
| Dissipation Factor | 1MHz | ASTM D150 | 0.020 |
| arc resistance | | ASTM D495 | PLC6 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 204 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 160 °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.2E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | MD：60to138°C | ASTME831 | 2.2E-05 cm/cm/°C |
| RTI Elec | | UL 746 | 125 °C |
| RTI Imp | | UL 746 | 110 °C |
| RTI Str | | UL 746 | 125 °C |