TPE DGR 6060NC USA Advanced

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Permanent compression deformation	70°C,22hr	ASTM D395B	43	%
	Permanent compression deformation	100°C,22hr	ASTM D395B	71	%
	Permanent compression deformation	Permanent compression deformation	24°C,22hr	ISO 815	23	%
tensile strength	Yield,23°C	ASTM D412	7.42	MPa
	tensile strength	100%Strain,23°C	ISO 37	2.19	MPa
	tensile strength	tensile strength	100%Strain	ASTM D412	2.19	MPa
Stretch permanent deformation	100%Strain	ASTM D412	11	%
Permanent compression deformation	24°C,22hr	ASTM D395B	23	%
tear strength	24°C	ASTM D624	23.1	kN/m
elongation	Break,23°C	ISO 37	380	%
elongation	elongation	Break	ASTM D412	380	%
tensile strength	Yield,23°C	ISO 37	7.42	MPa
Permanent compression deformation	70°C,22hr	ISO 815	43	%
Permanent compression deformation	Permanent compression deformation	100°C,22hr	ISO 815	71	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Taber wear resistance	1000Cycles,1.0E+6g,CS-17Wheel	ASTM D1044	30.0	mg
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Brittle temperature		ASTM D746	-67.2	°C
Brittle temperature	Brittle temperature		ISO 812	-67.2	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183	0.988	g/cm³
density	density		ASTM D792	0.988	g/cm³
Shrinkage rate	MD：1.59mm	ASTM D955	2.2	%
	Shrinkage rate	MD：3.18mm	ASTM D955	1.3	%
		Shrinkage rate	TD：1.59mm	ASTM D955	1.5	%
			Shrinkage rate	TD：3.18mm	ASTM D955	1.0	%
				Shrinkage rate	TD:1.59mm	ISO 294-4	1.5	%
					Shrinkage rate	MD:1.59mm	ISO 294-4	2.2	%
						Shrinkage rate	TD:3.18mm	ISO 294-4	1.0	%
						Shrinkage rate	Shrinkage rate	MD:3.18mm	ISO 294-4	1.3	%
MeltViscosity	190°C,300sec^-1	ASTM D3835	107	Pa·s
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	ShoreA,5Sec	ASTM D2240	63
Shore hardness	Shore hardness	ShoreA,5Sec	ISO 868	63
aging	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume change	24°C,168hr,inReferenceFuelB	ASTM D471	9.0	%
Tensile stress change rate	100°C,168hr，Break	ISO 1817	0.0	%
Tensile stress change rate	Tensile stress change rate	70°C,168hr，Break	ISO 1817	-2.0	%
Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	5.0	%
Volume change	100°C,168hr,inIRM903Oil	ISO 1817	39	%
	Volume change	100°C,168hr,inASTM#1Oil	ISO 1817	2.0	%
		Volume change	24°C,168hr,inReferenceFuelB	ISO 1817	9.0	%
			Volume change	100°C,168hr,在水中	ASTM D471	-13	%
			Volume change	Volume change	100°C,168hr,inIRM903Oil	ASTM D471	39	%
Change rate of tensile strength in air	100°C,168hr	ASTM D573	-7.0	%
	Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	-1.0	%
		Change rate of tensile strength in air	70°C,168hr	ASTM D573	-12	%
			Change rate of tensile strength in air	70°C,168hr	ISO 188	-12	%
				Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	-1.0	%
					Change rate of tensile strength in air	100°C,168hr	ISO 188	-7.0	%
					Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	5.0	%
Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	-2.0	%
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	0.0	%
Volume change	100°C,168hr,inASTM#1Oil	ASTM D471	2.0	%
Volume change	Volume change	100°C,168hr,在水中	ISO 1817	-13	%