PP ISPLEN® PM 240 AT REPSOL

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Suspended wall beam without notch impact strength	23°C	ISO 180	40 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	0°C	ISO 180	30 kJ/m²
Impact strength of cantilever beam gap	0°C	ISO 180	3.3 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	5.0 kJ/m²

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	Yield	ISO 527-2	35.0 MPa
Tensile strain	Yield	ISO 527-2	5.0 %
Bending modulus		ISO 178	2800 MPa

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	120 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	66.0 °C
Vicat softening temperature	--	ISO 306/A120	154 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	98.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ISO 1183	1.04 g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	3.0 g/10min
Shrinkage rate		ISO 2577	0.90to1.5 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	ShoreD,15Sec	ISO 868	76

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.