PUR，Unspecified HYDEX® 202 ENSINGER GERMANY

مقایسه

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap		ASTM D256	530 J/m

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Friction coefficient	Itself - Static		0.26
Tensile modulus		ASTM D638	1650 MPa
tensile strength	Yield	ASTM D638	62.1 MPa
tensile strength	tensile strength	Break	ASTM D638	55.2 MPa
elongation	Yield	ASTM D638	9.0 %
elongation	elongation	Break	ASTM D638	80 %
Bending modulus		ASTM D790	1930 MPa
bending strength		ASTM D790	82.7 MPa
Friction coefficient	Itself - Dynamic		0.22

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	143 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	138 °C
Vicat softening temperature		ASTM D1525	144 °C
Linear coefficient of thermal expansion	MD	ASTM D696	6.7E-05 cm/cm/°C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.20 g/cm³
Water absorption rate	24hr	ASTM D570	0.21 %