برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.36 g/cm³ |
| density | | ISO 1183 | 1.36 g/cm³ |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 9.0 g/10min |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 9.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 1.7 % |
| Shrinkage rate | TD | ISO 294-4 | 2.1 % |
| Shrinkage rate | MD | ISO 294-4 | 2.1 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.55 % |
| Water absorption rate | 平衡,23°C,60%RH | ASTM D570 | 0.25 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M级 | ASTM D785 | 76 |
| Rockwell hardness | M级 | ISO 2039-2 | 89 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服,23°C | ISO 527-2 | 40.0 Mpa |
| elongation | 屈服,23°C | ASTM D638 | 85 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | >50 % |
| Flexural modulus | 23°C | ASTM D790 | 1700 Mpa |
| Flexural modulus | 23°C | ISO 178 | 1750 Mpa |
| bending strength | 23°C | ASTM D790 | 60.0 Mpa |
| bending strength | 23°C | ISO 178 | 50.0 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 43.0 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 110 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | IEC 60093 | 1E+14 ohms·cm |
| dielectric strength | | ASTM D149 | 19 KV/mm |
| dielectric strength | | IEC 60243-1 | 19 KV/mm |
| dielectric constant | | ASTM D150 | 3.70 |
| Dissipation Factor | 1MHz | ASTM D150 | 6E-03 |
| Surface Resistivity | | ASTM D257 | 1E+16 ohms |
| Surface Resistivity | | IEC 60093 | 1E+16 ohms |
| Volume resistivity | | ASTM D257 | 1E+14 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 144 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 82.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |
| melting temperature | | ISO 11357-3 | 166 °C |
| melting temperature | | | 166 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 1.3E-04 cm/cm/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه
مشاهده قیمت‌ها