Thermoset Premi-Glas® 3405 USA Premix
0
مقایسهبرگه داده فنی
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Tensile modulus | Compression Molded | ASTM D638 | 11700 MPa |
| tensile strength | Compression Molded | ASTM D638 | 82.7 MPa |
| Flexural modulus | Compression Molded | ASTM D790 | 8960 MPa |
| bending strength | Compression Molded | ASTM D790 | 190 MPa |
| Poisson's ratio | 0.30 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | Compression Molded | ASTM D256 | 1000 J/m |
| Suspended wall beam without notch impact strength | Compression Molded | ASTM D4812 | 1400 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| arc resistance | ASTM D495 | >180 sec | |
| Compared to the Leakage Tracking Index (CTI) | ASTM D2303 | PLC 0 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD2 | 2.5E-05 cm/cm/°C | |
| TD3 | 3.5E-05 cm/cm/°C | ||
| thermal conductivity | 0.30 W/m/K | ||
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI Str | UL 746 | 130 °C |