PC+Polyester XYLEX™ X8300 resin SABIC

مقایسه

برگه داده فنی

physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.20 g/cm³
density	density		ISO 1183	1.17 g/cm³
melt mass-flow rate	265°C/2.16kg	ASTM D1238	15 g/10min
Melt volume flow rate	265°C/2.16kg	ISO 1133	15.0 cm³/10min
Shrinkage rate	MD：3.20mm	内部方法	0.50to0.80 %
Shrinkage rate	Shrinkage rate	TD：3.20mm	内部方法	0.40to0.60 %
Water absorption rate	饱和,23°C	ISO 62	0.050 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.20 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	邵氏D,10秒	ASTM D2240	74

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
transmissivity	2540µm	ASTM D1003	88.0 %
Haze ratio	2540µm	ASTM D1003	1.0 %
refractive index		ISO 489	1.539

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	3.0mm	UL 94	V-2
Burning wire flammability index	1.0mm	IEC 60695-2-12	750 °C

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Flexural modulus	50.0mm跨距	ASTM D790	1680 MPa
Flexural modulus	Flexural modulus		ISO 178	1700 MPa
bending strength		ISO 178	78.0 MPa
bending strength	bending strength	屈服,50.0mm跨距	ASTM D790	71.0 MPa
tensile strength	Break	ASTM D638	46.0 MPa
tensile strength	tensile strength	Break	ISO 527-2/50	54.0 MPa
elongation	Yield	ASTM D638	5.0 %
Tensile strain	Yield	ISO 527-2/50	>5.0 %
elongation	Break	ASTM D638	150 %
Tensile strain	Break	ISO 527-2/50	>200 %
Tensile modulus		ASTM D638	1520 MPa
Tensile modulus	Tensile modulus		ISO 527-2/1	1600 MPa
tensile strength	Yield	ASTM D638	47.0 MPa
tensile strength	tensile strength	Yield	ISO 527-2/50	55.0 MPa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Impact strength of cantilever beam gap	-30°C	ASTM D256	73 J/m
	Impact strength of cantilever beam gap	23°C	ASTM D256	1100 J/m
		Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
			Impact strength of cantilever beam gap	-10°C	ISO 180/1A	5.0 kJ/m²
			Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	95.0 J

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		ASTM D257	>1.0E+15 ohms·cm
Compared to the Leakage Tracking Index (CTI)	CTI	UL 746	PLC 0
Surface Resistivity		ASTM D257	>1.0E+15 ohms

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa,未退火,3.20mm，HDT	ASTM D648	79.0 °C
	Heat distortion temperature	1.8MPa,未退火,3.20mm，HDT	ASTM D648	75.0 °C
		Heat distortion temperature	1.8MPa,未退火,100mm跨距9，HDT	ISO 75-2/Ae	80.0 °C
		Heat distortion temperature	Heat distortion temperature	1.8MPa,未退火,64.0mm跨距10，HDT	ISO 75-2/Af	78.0 °C
vicat		ASTM D152511	91.0 °C
vicat	vicat		ISO 306/B120	96.0 °C
ball-indentation hardness	85°C	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	MD：-40到40°C	ASTME831	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
		Linear coefficient of thermal expansion	MD：23to60°C	ISO 11359-2	9E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	1.1E-04 cm/cm/°C
				Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
				Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to60°C	ISO 11359-2	9E-05 cm/cm/°C
thermal conductivity		ISO 8302	0.23 W/m/K

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.