Fluorelastomer Viton® A-331C The Chemours Company
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 1.82 g/cm³ | |
| Apparent density | ASTM D1895 | 1.82 g/cm³ | |
| Mooney viscosity | ML1+10,121°C | ASTM D1646 | 65 MU |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Shore hardness | 邵氏A,23°C2 | ASTM D2240 | 75 |
| 邵氏A,23°C3 | ASTM D2240 | 72 | |
| 邵氏A,23°C4 | ASTM D2240 | 77 | |
| 邵氏A,23°C5 | ASTM D2240 | 76 | |
| 邵氏A,23°C | ASTM D2240 | 71 |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| tensile strength | 100%应变,23°C8 | ASTM D412 | 4.50 MPa |
| 100%应变,23°C9 | ASTM D412 | 4.50 MPa | |
| 100%应变,23°C6 | ASTM D412 | 3.10 MPa | |
| 100%应变,23°C7 | ASTM D412 | 4.60 MPa | |
| elongation | 断裂,23°C10 | ASTM D412 | 230 % |
| compression set | 23°C,70hr | ASTM D395B | 18 % |
| 200°C,70hr | ASTM D395B | 21 % | |
| 200°C,168hr | ASTM D395B | 29 % | |
| 232°C,70hr | ASTM D395B | 40 % | |
| tensile strength | 100%应变,23°C10 | ASTM D412 | 4.90 MPa |
| 屈服,23°C6 | ASTM D412 | 9.70 MPa | |
| 屈服,23°C7 | ASTM D412 | 14.5 MPa | |
| 屈服,23°C8 | ASTM D412 | 15.0 MPa | |
| 屈服,23°C9 | ASTM D412 | 13.5 MPa | |
| 屈服,23°C10 | ASTM D412 | 14.1 MPa | |
| elongation | 断裂,23°C6 | ASTM D412 | 350 % |
| 断裂,23°C7 | ASTM D412 | 240 % | |
| 断裂,23°C8 | ASTM D412 | 260 % | |
| 断裂,23°C9 | ASTM D412 | 240 % |