ULDPE NG 4701G DOW USA
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | ASTM D792 | 0.912 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.80 g/10min |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 45° | ASTM D2457 | 49 |
| Haze ratio | ASTM D1003 | 11 % |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| film strength | TD | ASTM D882 | 70.3 J/cm³ |
| Secant modulus | 1%正割,MD | ASTM D882 | 141 MPa |
| 2%正割,MD | ASTM D882 | 124 MPa | |
| 2%正割,TD | ASTM D882 | 131 MPa | |
| tensile strength | MD:屈服 | ASTM D882 | 8.96 MPa |
| TD:屈服 | ASTM D882 | 8.62 MPa | |
| MD:断裂 | ASTM D882 | 41.4 MPa | |
| TD:断裂 | ASTM D882 | 37.2 MPa | |
| elongation | MD:断裂 | ASTM D882 | 400 % |
| TD:断裂 | ASTM D882 | 450 % | |
| Dart impact | ASTM D1709B | 380 g | |
| Elmendorf tear strength | MD | ASTM D1922 | 250 g |
| Thin film puncture strength | 内部方法 | 6.21 J | |
| 内部方法 | 71.2 N | ||
| 内部方法 | 33.1 J/cm³ | ||
| film strength | MD | ASTM D882 | 72.8 J/cm³ |
| Elmendorf tear strength | TD | ASTM D1922 | 600 g |
| Secant modulus | 1%正割,TD | ASTM D882 | 148 MPa |
| film thickness | 25 µm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| vicat | ASTM D1525 | 99.0 °C | |
| melting temperature | ISO 3146 | 101 °C |