برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.1 % |
| Shrinkage rate | 流量 | ISO 294-4 | 0.35 % |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.75 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 5.4 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.6 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8 mm | UL 94 | HB |
| UL flame retardant rating | 1.6 mm | UL 94 | HB |
| UL flame retardant rating | 3.2 mm | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 23 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 11400 Mpa |
| tensile strength | 断裂, 23°C | ISO 527-2/1A | 210 Mpa |
| Tensile strain | 断裂, 23°C | ISO 527-2 | 3.0 % |
| Flexural modulus | 23°C | ASTM D790 | 9800 Mpa |
| Flexural modulus | 23°C | ISO 178 | 9500 Mpa |
| bending strength | 23°C | ASTM D790 | 290 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 90 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 80 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 6.0E+15 ohms |
| Volume resistivity | | IEC 60093 | 1.0E+15 ohms·cm |
| dielectric strength | 2.00 mm | IEC 60243-1 | 34 KV/mm |
| relative permittivity | | IEC 60250 | 3.70 |
| Dissipation Factor | | IEC 60250 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案 A | IEC 60112 | PLC 1 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 80 °C |
| Suggested maximum moisture content | | | 0.20 % |
| Temperature at the rear of the barrel | | | 270 to 280 °C |
| Temperature in the middle of the barrel | | | 275 to 285 °C |
| Temperature at the front of the material cylinder | | | 280 to 290 °C |
| Temperature | | | 70 to 100 °C |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 255 °C |
| melting temperature | | ISO 11357-3 | 263 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.