physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD：1.59mm	ASTM D955	1.4 %
	Shrinkage rate	MD：3.18mm	ASTM D955	1.3 %
		Shrinkage rate	TD：1.59mm	ASTM D955	0.50 %
			Shrinkage rate	TD：3.18mm	ASTM D955	1.1 %
				Shrinkage rate	TD:1.59mm	ISO 294-4	0.50 %
					Shrinkage rate	MD:1.59mm	ISO 294-4	1.4 %
						Shrinkage rate	TD:3.18mm	ISO 294-4	1.1 %
						Shrinkage rate	Shrinkage rate	MD:3.18mm	ISO 294-4	1.3 %
MeltViscosity	190°C,300sec^-1	ASTM D3835	219 Pa·s

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Shore hardness	邵氏A,5秒	ASTM D2240	78
Shore hardness	Shore hardness	邵氏A,5秒	ISO 868	78

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Taber wear resistance	1000Cycles,1.0E+6g,CS-17Wheel	ASTM D1044	12.5 mg

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون
Stretch permanent deformation	100%应变	ASTM D412	16 %
tensile strength	100%应变	ASTM D412	2.54 Mpa
	tensile strength	100%应变,23°C	ISO 37	2.54 Mpa
		tensile strength	屈服,23°C	ASTM D412	8.30 Mpa
		tensile strength	tensile strength	屈服,23°C	ISO 37	8.30 Mpa
elongation	断裂	ASTM D412	310 %
elongation	elongation	断裂,23°C	ISO 37	310 %
tear strength	24°C	ASTM D624	33.4 kN/m
compression set	24°C,22hr	ASTM D395B	26 %
	compression set	70°C,22hr	ASTM D395B	48 %
		compression set	100°C,22hr	ASTM D395B	63 %
			compression set	24°C,22hr	ISO 815	26 %
				compression set	70°C,22hr	ISO 815	48 %
				compression set	compression set	100°C,22hr	ISO 815	63 %

aging	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile stress change rate	70°C,168hr，断裂	ISO 1817	-5.0 %
Tensile stress change rate	Tensile stress change rate	100°C,168hr，断裂	ISO 1817	4.0 %
volume change	24°C,168hr,inReferenceFuelB	ASTM D471	54 %
	volume change	100°C,168hr,inASTM#1Oil	ASTM D471	6.0 %
		volume change	100°C,168hr,inIRM903Oil	ASTM D471	82 %
			volume change	100°C,168hr,在水中	ASTM D471	1.0 %
				volume change	24°C,168hr,inReferenceFuelB	ISO 1817	54 %
					volume change	100°C,168hr,inASTM#1Oil	ISO 1817	6.0 %
						volume change	100°C,168hr,inIRM903Oil	ISO 1817	82 %
						volume change	volume change	100°C,168hr,在水中	ISO 1817	1.0 %
Change rate of tensile strength in air	70°C,168hr	ASTM D573	-2.0 %
	Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	7.0 %
		Change rate of tensile strength in air	100°C,168hr	ASTM D573	-2.0 %
			Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	7.0 %
				Change rate of tensile strength in air	70°C,168hr	ISO 188	-2.0 %
					Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	7.0 %
						Change rate of tensile strength in air	100°C,168hr	ISO 188	-2.0 %
						Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	7.0 %
Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	-5.0 %
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	4.0 %

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
brittle temperature		ASTM D746	-61.1 °C
brittle temperature	brittle temperature		ISO 812	-61.1 °C