Copolyester Tritan™ MX811 Eastman Chemical Company

مقایسه

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
transmissivity	Total	ASTM D1003	92.0 %
turbidity		ASTM D1003	<1.0 %

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of cantilever beam gap	23°C	ASTM D256	650 J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ASTM D4812	NoBreak

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Bending modulus	23°C	ASTM D790	1590 MPa
bending strength	Yield,23°C	ASTM D790	66.0 MPa
Tensile modulus	23°C	ASTM D638	1590 MPa
tensile strength	Yield,23°C	ASTM D638	44.0 MPa
tensile strength	tensile strength	Break,23°C	ASTM D638	53.0 MPa
elongation	Yield,23°C	ASTM D638	7.0 %
elongation	elongation	Break,23°C	ASTM D638	140 %

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	109 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	92.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
density		ASTM D792	1.17 g/cm³
Shrinkage rate	MD	ASTM D955	0.50to0.70 %

hardness	شرایط آزمون	روش آزمون	نتیجه آزمون
Rockwell hardness	R-Sale,23°C	ASTM D785	115