| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTMD792 | 1.16 g/cm³ |
| Shrinkage rate | | 内部方法 | 1.2 % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Limiting Oxygen Index | | ASTMD2863 | >30 % |
| Hot filament ignition temperature | 1.5mm | IEC 60695-2-13 | 775 °C |
| Hot filament ignition temperature | 0.75mm | IEC 60695-2-13 | 775 °C |
| Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | 0.75mm | IEC 60695-2-12 | 850 °C |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | Break | ASTMD638 | 80.0 MPa |
| elongation | Break | ASTMD638 | 25 % |
| Flexural modulus | | ASTMD790 | 3200 MPa |
| bending strength | -- | ISO 178 | 95.0 MPa |
| bending strength | Break | ASTM D790 | 95.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | | ISO 180 | 3.5 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| dielectric strength | | ASTMD149 | 37 kV/mm |
| Volume resistivity | | ASTMD257 | 1E+15 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTMD648 | 200 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 75.0 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 6.5E-05 cm/cm/°C |
| melting temperature | | ISO 1218 | 218 °C |