Plastomer, Ethylene-based Premi-Glas® 1205 USA Premix
0
مقایسهبرگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| density | 1.80 g/cm³ | ||
| Shrinkage rate | MD | 0.040 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Impact strength of cantilever beam gap | Compression Molded | ASTM D256 | 530 J/m |
| Suspended wall beam without notch impact strength | Compression Molded | ASTM D4812 | 640 J/m |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| elongation | Break | ASTM D638 | 0.80 % |
| Flexural modulus | Compression Molded | ASTM D790 | 10300 MPa |
| Tensile modulus | Compression Molded | ASTM D638 | 10300 MPa |
| tensile strength | Compression Molded | ASTM D638 | 41.4 MPa |
| bending strength | Compression Molded | ASTM D790 | 110 MPa |
| Poisson's ratio | 0.30 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD2 | 2.5E-05 cm/cm/°C | |
| TD3 | 3.5E-05 cm/cm/°C | ||
| thermal conductivity | 0.30 W/m/K |