PA Generic Nylon, Unspecified Generic

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
turbidity		ASTM D1003	0.60to1.1	%
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	23°C	ISO 179	4.0to14	kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	10to130	J/m
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	4.0to85	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Bending modulus	23°C	ASTM D790	305to12700	MPa
Nominal tensile fracture strain	23°C	ISO 527-2	50to57	%
elongation	Break,23°C	ISO 527-2	2.0to200	%
elongation	elongation	Break,23°C	ASTM D638	0.70to51	%
Bending modulus	23°C	ISO 178	275to3250	MPa
bending strength	23°C	ASTM D790	50.5to153	MPa
	bending strength	23°C	ISO 178	13.5to152	MPa
	bending strength	bending strength	Yield,23°C	ASTM D790	73.6to304	MPa
Friction coefficient		ASTM D1894	0.20to1.0
Tensile modulus	23°C	ASTM D638	500to4240	MPa
Tensile modulus	Tensile modulus	23°C	ISO 527-2	590to3290	MPa
tensile strength	Yield,23°C	ASTM D638	22.6to186	MPa
	tensile strength	Yield,23°C	ISO 527-2	40.0to114	MPa
		tensile strength	Break,23°C	ASTM D638	39.0to64.9	MPa
			tensile strength	Break,23°C	ISO 527-2	40.0to74.0	MPa
			tensile strength	tensile strength	23°C	ASTM D638	50.7to69.9	MPa
elongation	Yield,23°C	ASTM D638	2.5to60	%
elongation	elongation	Yield,23°C	ISO 527-2	5.0to8.5	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
thermal conductivity	23°C	ASTMC177	0.22to3.8	W/m/K
Linear coefficient of thermal expansion	TD	ISO 11359-2	7.9E-5到1.3E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD	ISO 11359-2	8.9E-5到1.3E-4	cm/cm/°C
Melting temperature	--	ISO 3146	190to250	°C
Glass transition temperature		ISO 11357-2	140	°C
Vicat softening temperature		ISO 306	125to137	°C
Melting temperature	--		198to260	°C
Melting temperature	Melting temperature	--	ISO 11357-3	55.0to260	°C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	117to197	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	113to161	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	52.9to266	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	59.7to147	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.90to2.0	%
	Water absorption rate	Saturation,23°C	ISO 62	3.3to8.6	%
	Water absorption rate	Water absorption rate	23°C,24hr	ASTM D570	0.27to1.3	%
Shrinkage rate	23°C	ISO 294-4	7.5E-3-2.6	%
	Shrinkage rate	TD:23°C	ASTM D955	0.67to2.6	%
	Shrinkage rate	Shrinkage rate	MD:23°C	ASTM D955	0.20to3.7	%
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.6to29	g/10min
density	23°C	ISO 1183	1.02to1.18	g/cm³
density	density	--	ASTM D792	1.01to1.45	g/cm³
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Relative permittivity	23°C	IEC 60250	4.80
Dielectric strength	23°C	IEC 60243-1	14to28	kV/mm
Volume resistivity	23°C	IEC 60093	1.0E+12到1.0E+16	ohms·cm
Volume resistivity	Volume resistivity	23°C	ASTM D257	4.0E+8到1.0E+16	ohms·cm
Surface resistivity	--	IEC 60093	1.0E+11到1.0E+15	ohms
Surface resistivity	Surface resistivity	--	ASTM D257	1.0E+5到1.0E+14	ohms
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dissipation factor	23°C	IEC 60250	0.012to0.15
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	23°C	ISO 868	75to82
Rockwell hardness	23°C	ASTM D785	71to118