برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D1505 | 0.900 g/cm³ |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 1.4 g/10min |
| density | | ASTM D1505 | 0.900 g/cm³ |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 1.4 g/10min |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 64 |
| Rockwell hardness | R-Scale | ASTM D785 | 64 |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Fluidity-HPC | HPC | | 940 mm |
| Fluidity-HPC | HPC | | 940 mm |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | Break | ASTM D638 | 450 % |
| Flexural modulus | | ASTM D790 | 1150 MPa |
| Flexural modulus | | ASTM D790 | 1150 MPa |
| tensile strength | Yield | ASTM D638 | 27.0 MPa |
| tensile strength | Yield | ASTM D638 | 27.0 MPa |
| elongation | Break | ASTM D638 | 450 % |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 29 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | >500 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 29 J/m |
| Suspended wall beam without notch impact strength | 23°C | ASTM D256 | >500 J/m |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| vicat | | ASTM D1525 | 135 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| vicat | | ASTM D1525 | 135 °C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.