TPE DGR 6170BK USA Advanced

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
elongation	Break	ASTM D412	420	%
elongation	elongation	Break,23°C	ISO 37	420	%
tensile strength	Yield,23°C	ISO 37	9.24	MPa
	tensile strength	Yield,23°C	ASTM D412	9.24	MPa
		tensile strength	100%Strain,23°C	ISO 37	2.76	MPa
		tensile strength	tensile strength	100%Strain	ASTM D412	2.76	MPa
Stretch permanent deformation	100%Strain	ASTM D412	5	%
Permanent compression deformation	70°C,22hr	ISO 815	82	%
	Permanent compression deformation	24°C,22hr	ISO 815	21	%
		Permanent compression deformation	100°C,22hr	ASTM D395B	95	%
		Permanent compression deformation	Permanent compression deformation	100°C,22hr	ISO 815	95	%
tear strength	24°C	ASTM D624	37.0	kN/m
Permanent compression deformation	24°C,22hr	ASTM D395B	21	%
Permanent compression deformation	Permanent compression deformation	70°C,22hr	ASTM D395B	82	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Taber wear resistance	1000Cycles,1.0E+6g,CS-17Wheel	ASTM D1044	87.0	mg
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Brittle temperature		ASTM D746	-67.8	°C
Brittle temperature	Brittle temperature		ISO 812	-67.8	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	TD:1.59mm	ISO 294-4	0.0	%
	Shrinkage rate	TD：3.18mm	ASTM D955	0.40	%
		Shrinkage rate	TD：1.59mm	ASTM D955	0.0	%
			Shrinkage rate	MD：3.18mm	ASTM D955	1.3	%
			Shrinkage rate	Shrinkage rate	MD：1.59mm	ASTM D955	0.90	%
MeltViscosity	190°C,300sec^-1	ASTM D3835	420	Pa·s
Shrinkage rate	MD:1.59mm	ISO 294-4	0.90	%
	Shrinkage rate	TD:3.18mm	ISO 294-4	0.40	%
	Shrinkage rate	Shrinkage rate	MD:3.18mm	ISO 294-4	1.3	%
density		ISO 1183	1.10	g/cm³
density	density		ASTM D792	1.10	g/cm³
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	ShoreA,5Sec	ASTM D2240	65
Shore hardness	Shore hardness	ShoreA,5Sec	ISO 868	65
aging	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume change	70°C,168hr,inWater	ISO 1817	1.0	%
	Volume change	70°C,168hr,inIRM903Oil	ISO 1817	42	%
		Volume change	70°C,168hr,inASTM#1Oil	ISO 1817	5.0	%
			Volume change	24°C,168hr,inReferenceFuelB	ISO 1817	49	%
				Volume change	70°C,168hr,inWater	ASTM D471	1.0	%
					Volume change	70°C,168hr,inIRM903Oil	ASTM D471	42	%
						Volume change	70°C,168hr,inASTM#1Oil	ASTM D471	5.0	%
						Volume change	Volume change	24°C,168hr,inReferenceFuelB	ASTM D471	49	%
Change rate of tensile strength in air	100°C,168hr	ASTM D573	41	%
	Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	-3.0	%
		Change rate of tensile strength in air	70°C,168hr	ISO 188	34	%
			Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	5.0	%
				Change rate of tensile strength in air	100°C,168hr	ISO 188	41	%
				Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	-3.0	%
Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	8.0	%
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	18	%
Tensile stress change rate	70°C,168hr，Break	ISO 1817	8.0	%
Tensile stress change rate	Tensile stress change rate	100°C,168hr，Break	ISO 1817	18	%
Change rate of tensile strength in air	70°C,168hr	ASTM D573	34	%
Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	5.0	%