ASA/PC GELOY™ HRA222F SABIC INNOVATIVE US

ویژگی‌ها:
مقاومت در برابر دمای بالاثبات حرارتی
کاربردها:
قطعات لوازم خانگیتجهیزات باغ چمن
گواهی‌نامه‌ها:
UL
مقایسه مشاهده قیمت‌ها

برگه داده فنی

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	2.0 mm	UL 94	V-0
Extreme Oxygen Index		ISO 4589-2	29 %

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	--3	ASTM D638	2590 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2520 Mpa
tensile strength	Yield4	ASTM D638	63.0 Mpa
	tensile strength	Yield5	ASTM D638	59.0 Mpa
		tensile strength	Yield	ISO 527-2/5	62.0 Mpa
			tensile strength	Yield	ISO 527-2/50	60.0 Mpa
				tensile strength	Break5	ASTM D638	66.0 Mpa
					tensile strength	Break4	ASTM D638	56.0 Mpa
						tensile strength	Break	ISO 527-2/5	51.0 Mpa
						tensile strength	tensile strength	Break	ISO 527-2/50	45.0 Mpa
elongation	Yield5	ASTM D638	4.2 %
	elongation	Yield4	ASTM D638	4.3 %
		elongation	Yield	ISO 527-2/5	4.3 %
			elongation	Yield	ISO 527-2/50	4.4 %
				elongation	Break5	ASTM D638	> 100 %
					elongation	Break4	ASTM D638	> 100 %
					elongation	elongation	Break	ISO 527-2/5	> 50 %
Bending modulus		ISO 178	2510 Mpa
bending strength		ISO 178	93.0 Mpa

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Suggested maximum moisture content			0.020 %
Hopper temperature			60 to 80 °C
Temperature at the rear of the barrel			200 to 230 °C
Temperature in the middle of the barrel			220 to 260 °C
Temperature at the front of the material cylinder			230 to 270 °C
Spray nozzle temperature			220 to 260 °C
Processing (melt) temperature			230 to 270 °C
Mold temperature			50 to 70 °C

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Be	99.0 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span	ISO 75-2/Ae	88.0 °C
Vicat softening temperature	--	ISO 306/A50	111 °C
	Vicat softening temperature	--	ISO 306/B50	102 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	104 °C
Ball Pressure Test	73 to 77°C	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -30 to 80°C	ISO 11359-2	6.9E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Across Flow : -30 to 80°C	ISO 11359-2	7.1E-5 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	7.5E-5 cm/cm/°C
RTI Elec		UL 746	90.0 °C
RTI Imp		UL 746	90.0 °C
RTI		UL 746	90.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Melt Volume Flow Rate (MVR)	260°C/2.16 kg	ISO 1133	13.0 cm3/10min
Shrinkage rate	Flow	Internal Method	0.40 - 0.60 %
Water absorption rate	Saturation, 23°C	ISO 62	0.60 %
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.20 %
Outdoor applicability		UL 746C	f1

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Compared to the anti leakage trace index		UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index		IEC 60112	PLC 0

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.