PP MAJORIS FFR037 - 1298 AD MAJORIS FRANCE

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Charpy Notched Impact Strength	-20°C	ISO 179/1eA	2.2	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	5.5	kJ/m²
Impact strength of simply supported beam without notch	-20°C	ISO 179/1eU	71	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	190	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	1.5mm	UL 94	V-2
Burning wire flammability index	0.50mm	IEC 60695-2-12	850	°C
	Burning wire flammability index	1.0mm	IEC 60695-2-12	850	°C
		Burning wire flammability index	2.0mm	IEC 60695-2-12	960	°C
		Burning wire flammability index	Burning wire flammability index	3.0mm	IEC 60695-2-12	960	°C
Extreme Oxygen Index		ISO 4589-2	24	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2	1500	MPa
tensile strength	Yield	ISO 527-2/50	28.0	MPa
tensile strength	tensile strength	Break	ISO 527-2	12.0	MPa
Tensile strain	Yield	ISO 527-2/50	6.0	%
Tensile strain	Tensile strain	Break	ISO 527-2	80	%
Bending modulus		ISO 178	1400	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	94.0	°C
Vicat softening temperature	--	ISO 306/A	154	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B	79.0	°C
Ball Pressure Test	125°C	IEC 60335-1	通过
RTI Elec		UL 746	110	°C
RTI Imp		UL 746	115	°C
RTI		UL 746	115	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD:2.00mm	ISO 294-4	1.2	%
density		ISO 1183	0.945	g/cm³
melt mass-flow rate	230°C/2.16kg	ISO 1133	18	g/10min
Spiral flow length			102	cm
Shrinkage rate	TD	ISO 294-4	1.2	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dissipation factor	1kHz	IEC 60250	1.5E-03
Dissipation factor	Dissipation factor	100kHz	IEC 60250	2E-03
Arc resistance	3.00mm	ASTM D495	PLC 5
Compared to the anti leakage trace index	3.00mm	UL 746	PLC 0
Compared to the anti leakage trace index	Compared to the anti leakage trace index	--	IEC 60112	PLC 0
Dielectric strength		IEC 60243-1	41	kV/mm
Relative permittivity	50Hz	IEC 60250	2.25
	Relative permittivity	1kHz	IEC 60250	2.25
	Relative permittivity	Relative permittivity	100kHz	IEC 60250	2.24
Dissipation factor	50Hz	IEC 60250	1.5E-03
Compared to the anti leakage trace index	SolutionB	IEC 60112	PLC 0
Needle flame test	1.00mm	IEC 60695-11-5	通过
High arc combustion index	1.5mm	UL 746	PLC 0
High arc combustion index	High arc combustion index	3.0mm	UL 746	PLC 0
High voltage arc tracing rate	1.50mm	UL 746	PLC 0
High voltage arc tracing rate	High voltage arc tracing rate	3.00mm	UL 746	PLC 0
Hot wire ignition	1.5mm	UL 746	PLC 3
Hot wire ignition	Hot wire ignition	3.0mm	UL 746	PLC 2
Surface resistivity		IEC 60093	7.8E+15	ohms
Volume resistivity		IEC 60093	2E+16	ohms·cm