برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.20 g/cm³ |
| density | | ISO 1183 | 1.20 g/cm³ |
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.50to0.70 % |
| Water absorption rate | 24hr | ASTM D570 | 0.13 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.13 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 117 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | 总计 | ASTM D1003 | 81.0 % |
| transmissivity | Regular | ASTM D1003 | 77.0 % |
| Haze ratio | | ASTM D1003 | 3.6 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | V-2 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -40°C | ASTM D4812 | NoBreak |
| Impact strength of cantilever beam gap | 23°C | ASTM D4812 | NoBreak |
| Dart impact | -40°C,EnergyatPeakLoad | ASTM D3763 | 46.0 J |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 51.0 J |
| Multi axis Instrumented Impact Energy | -40°C,能量到力量峰值 | ISO 6603-2 | 23.0 J |
| Multi axis Instrumented Impact Energy | 23°C,能量到力量峰值 | ISO 6603-2 | 19.0 J |
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 75 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | NoBreak |
| Impact strength of cantilever beam gap | -40°C | ISO 180 | 8.3 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 10 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | 4.00mm | ISO 178 | 81.0 MPa |
| bending strength | Yield | ASTM D790 | 86.0 MPa |
| tensile strength | Break | ASTM D638 | 60.0 MPa |
| tensile strength | 断裂,4.00mm | ISO 527-2 | 56.0 MPa |
| elongation | Yield | ASTM D638 | 6.0 % |
| Tensile strain | Yield,4.00mm | ISO 527-2 | 5.4 % |
| elongation | Break | ASTM D638 | 150 % |
| Tensile strain | 断裂,4.00mm | ISO 527-2 | 130 % |
| Flexural modulus | | ASTM D790 | 2140 MPa |
| Flexural modulus | 4.00mm | ISO 178 | 2100 MPa |
| tensile strength | Yield | ASTM D638 | 56.0 MPa |
| tensile strength | 屈服,4.00mm | ISO 527-2 | 56.0 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dissipation Factor | 1kHz | ASTM D150 | 2E-03 |
| Dissipation Factor | 1MHz | ASTM D150 | 8E-03 |
| arc resistance | | ASTM D495 | 143 sec |
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | | ASTM D149 | 17 kV/mm |
| dielectric constant | 1kHz | ASTM D150 | 2.30 |
| dielectric constant | 1MHz | ASTM D150 | 2.10 |
| Compared to the Leakage Tracking Index (CTI) | | ASTM D3638 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 2 mm/min |
| Surface Resistivity | | ASTM D257 | 1E+16 ohms |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 103 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 103 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 90.0 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 90.0 °C |
| vicat | | ASTM D15252 | 118 °C |
| vicat | -- | ISO 306/A | 118 °C |
| vicat | -- | ISO 306/B | 110 °C |
| specific heat | 60°C | DSC | 1380 J/kg/°C |
| specific heat | 240°C | DSC | 2180 J/kg/°C |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.