برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | 23°C | ISO 1183 | 1.36 g/cm³ |
| Shrinkage rate | TD:23°C | ISO 294-4 | 0.60 % |
| Shrinkage rate | MD:23°C | ISO 294-4 | 0.30 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.0 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 6.5 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 0.8mm | IEC 60695-2-12 | 650 °C |
| Burning wire flammability index | 3.2mm | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 23 % |
| flammability | | FMVSS302 | B50 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 12 kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.0 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 13 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 50 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/A | 9.5 kJ/m² |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 3.0 % |
| Tensile modulus | 23°C | ISO 527-2 | 9400 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 175 MPa |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | 21 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 3.20mm,解决方案A | IEC 60112 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 221 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 210 °C |
| Continuous use temperature | | IEC 60216 | 130 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه