Basic Performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183/B	1.26
Water absorption rate	24hr,23℃	ISO 62	0.0100	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile stress	Yield	ISO 527-2	115	Mpa
Fracture strain		ISO 527-2	2.0	%
Bending modulus		ISO 178	9000	Mpa
bending strength		ISO 178	175	Mpa
Charpy Notched Impact Strength		ISO 179	9.00	KJ/m
Impact strength of simply supported beam without notch		ISO 179	34.0	KJ/m
Impact strength of cantilever beam gap		ISO 180	9.00	KJ/m
Suspended wall beam without notch impact strength		ISO 180	46.0	KJ/m
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa，Unannealed	ISO 75-2/B	260	°C
Hot deformation temperature	Hot deformation temperature	1.80MPa，Unannealed	ISO 75-2/A	240	°C
Vicat softening temperature		ISO 306	260	°C
UL flame retardant rating	1.50mm	UL 94	HB
RTI Str	1.50mm	UL 746	110	°C
RTI Imp	1.50mm	UL 746	110	°C
RTI Elec	1.50mm	UL 746	110	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	Across,Flow,1.60mm	ISO 294-4	0.20-1.00	%
Shrinkage rate	Shrinkage rate	Flow,1.60mm	ISO 294-4	0.10-0.30	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Dielectric constant		IEC 60250	3.100
Dielectric loss		IEC 60250	0.00100
Dielectric strength		IEC 60243-1	28.00	KV/mm