| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.13 g/cm³ |
| melt mass-flow rate | 230°C/2.16kg | ASTM D1238 | 4.0 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.40 % |
| intrinsic viscosity | 23°C | 内部方法 | 1.2 |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shore hardness | 邵氏A,23°C | ASTM D2240 | 95 |
| Shore hardness | 邵氏D,23°C | ASTM D2240 | 55 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| gloss | 45°,130µm | ASTM D2457 | 73 |
| refractive index | | ASTM D542 | 1.510 |
| transmissivity | 常规,130µm | ASTM D1003 | 91.0 % |
| transmissivity | 总计,130µm | ASTM D1003 | 94.0 % |
| Haze ratio | 130µm | ASTM D1003 | 1.0 % |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tear strength | 23°C | ASTM D1004 | 350 N |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ASTM D638 | 170 MPa |
| tensile strength | 屈服,23°C,3.00mm,注塑3 | ASTM D638 | 13.0 MPa |
| tensile strength | 断裂,23°C,2.00mm4 | ASTM D638 | 23.0 MPa |
| elongation | 屈服,23°C | ASTM D638 | 38 % |
| elongation | 断裂,23°C | ASTM D638 | 400 % |
| Flexural modulus | 23°C | ASTM D790 | 150 MPa |
| coefficient of friction | | ASTM D1894 | >1.0 |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -40°C | ASTM D256 | 40 J/m |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Kappa modulus | -70°C | ASTM D1043 | 930 MPa |
| Kappa modulus | -28°C | ASTM D1043 | 240 MPa |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | TD:屈服,130µm | ASTM D882 | 20 % |
| elongation | MD:断裂,130µm | ASTM D882 | 330 % |
| elongation | TD:断裂,130µm | ASTM D882 | >550 % |
| OTr | 30°C,130µm | ASTM D1434 | 940 cm³/m²/24hr |
| Water Vapor Transmission Rate | | ASTMF372 | 150 g/m²/24hr |
| film thickness | | | 130 µm |
| Secant modulus | 正切,MD:130µm | ASTM D882 | 197 MPa |
| Secant modulus | 正切,TD:130µm | ASTM D882 | 221 MPa |
| tensile strength | TD:屈服,130µm | ASTM D882 | 11.2 MPa |
| tensile strength | MD:断裂,130µm | ASTM D882 | 41.5 MPa |
| tensile strength | TD:断裂,130µm | ASTM D882 | 18.1 MPa |
| elongation | MD:屈服,130µm | ASTM D882 | 46 % |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Fusion temperature | 23°C | ASTME793 | 27.0 kJ/kg |
| brittle temperature | | ASTM D746 | <-75.0 °C |
| Glass Transition Temperature | | DSC | -3.00 °C |
| vicat | | ASTM D15256 | 170 °C |
| melting temperature | | ASTM D3418 | 205 °C |
| Crystallization peak temperature | DSC | DSC | 140 °C |
| Linear coefficient of thermal expansion | MD：23°C | ASTM D696 | 1.5E-04 cm/cm/°C |
| specific heat | 25°C7 | DSC | 1600 J/kg/°C |
| specific heat | 100°C7 | DSC | 1800 J/kg/°C |
| specific heat | 150°C7 | DSC | 2000 J/kg/°C |
| specific heat | 175°C7 | DSC | 2300 J/kg/°C |
| specific heat | 200°C8 | DSC | 3100 J/kg/°C |
| specific heat | 225°C9 | DSC | 2300 J/kg/°C |
| thermal conductivity | 23°C | ASTMC177 | 0.19 W/m/K |