HIPS SEHI-103 IDEMITSU MALASIA

ویژگی‌ها:
Characteristics high impact resistance flame retardant form particles
مقایسه

برگه داده فنی

flammability	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating	1.60 mm	UL 94	V-0

squeeze out	شرایط آزمون	روش آزمون	نتیجه آزمون
Oral mold temperature			190 to 220 °C
Material barrel temperature			200 to 240 °C
	Material barrel temperature			200 to 240 °C
		Material barrel temperature			180 to 220 °C
		Material barrel temperature	Material barrel temperature			160 to 200 °C
drying time			1.0 to 2.0 hr
drying temperature			70.0 °C

mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
elongation	Break	ASTM D638	20 %
tensile strength	Break	ASTM D638	18.6 MPa

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
Temperature at the rear of the barrel			180 to 210 °C
drying time			1.0 to 2.0 hr
drying temperature			70.0 °C
Mold temperature			40.0 to 60.0 °C
Spray nozzle temperature			200 to 230 °C
Temperature at the front of the material cylinder			210 to 240 °C
Temperature in the middle of the barrel			190 to 220 °C

thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	73.0 °C

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
melt mass-flow rate	200°C/5.0 kg	ASTM D1238	4.0 g/10 min
density		ASTM D792	1.17 g/cm³