برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Apparent density | | ISO 60 | 0.70 g/cm³ |
| Shrinkage rate | TD:280°C,3.00mm2 | ISO 2577 | 1.3 % |
| Shrinkage rate | TD:120°C,4hr,3.00mm3 | ISO 2577 | 0.070 % |
| Shrinkage rate | MD:290°C,3.00mm2 | ISO 2577 | 0.35 % |
| Shrinkage rate | MD:120°C,4hr,3.00mm3 | ISO 2577 | 0.040 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 5.5 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 650 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 25 % |
| Burning Behavior | | ISO 3795 | passed |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| ISO Shortcut | | ISO 1874 | PA66.GHWR.14-090.GF30 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Bending Strain | 23°C | ISO 178/A | 4.5 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 9500 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/5 | 180 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 4.0 % |
| Flexural modulus | 23°C | ISO 178/A | 8400 Mpa |
| bending strength | 3.5%Strain,23°C | ISO 178/A | 255 Mpa |
| bending strength | 23°C4 | ISO 178/A | 260 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 65 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 75 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 60 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 70 kJ/m² |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | 23°C,1.00mm | IEC 60243-1 | 35 KV/mm |
| relative permittivity | 23°C,100Hz | IEC 60250 | 4.00 |
| relative permittivity | 23°C,1MHz | IEC 60250 | 3.60 |
| Dissipation Factor | 23°C,100Hz | IEC 60250 | 8E-03 |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 0.016 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | V |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 250 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 245 °C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 125 °C |
| vicat | | ISO 306/B120 | >230 °C |
| melting temperature | | ISO 11357-3 | 262 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 3E-05 cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO 11359-2 | 9E-05 cm/cm/°C |