EVA UL00218 Lianhong Group

ویژگی‌ها:
Without adding opening agents and smoothing agents
with antioxidants
the recommended processing temperature range is 100 ℃ -190 ℃
the recommended processing temperature should not exceed 240 ℃
a typical foaming temperature of 175 ℃
a typical blowing temperature of 170 ℃
and the specific process design should be adjusted according to the equipment and product
کاربردها:
Suitable for foaming
injection molding
and extrusion products
مقایسه

برگه داده فنی

physical property	روش آزمون	نتیجه آزمون
density	ExxonMobil 方法	0.941 g/cm3
melt mass-flow rate	ASTM D1238	2.5 g/10min
Vinyl acetate content	ExxonMobil 方法	18 wt%

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Nominal fracture strain		GB/T 1040.2-2006	800 %
Shore hardness	A法，15s	GB/T 2411-2008	88
Tensile stress	断裂	GB/T 1040.2-2006	16 MPa

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
melting temperature		ASTM D3418	86 ℃
vicat		ASTM D31525	62 ℃

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.