impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	11	kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	65	kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	55	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	47	kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	13	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11	kJ/m²
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile strain	Break	ISO 527-2/5	3.0	%
tensile strength	Break	ISO 527-2/5	175	MPa
Tensile modulus		ISO 527-2/1	8600	MPa
bending strength		ISO 178	250	MPa
Bending modulus		ISO 178	7000	MPa
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Vicat softening temperature		ISO 306/B120	250	°C
Hot deformation temperature	1.8MPa,Unannealed,60.0mmSpan	ISO 75-2/A	245	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Stickiness	H2SO4（硫酸）)	ISO 307	150	cm³/g
density		ISO 1183	1.30	g/cm³