TPE DGR 6150BK USA Advanced

توصیف محصول

گواهی‌نامه‌ها(0)

جدول خواص

توصیف محصول

گواهی‌نامه‌ها

No Data...

برگه داده فنی

elastomer	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
tensile strength	Yield,23°C	ASTM D412	5.86	MPa
	tensile strength	100%Strain,23°C	ISO 37	1.79	MPa
	tensile strength	tensile strength	100%Strain	ASTM D412	1.79	MPa
Stretch permanent deformation	100%Strain	ASTM D412	3	%
tear strength	24°C	ASTM D624	25.6	kN/m
elongation	Break,23°C	ISO 37	360	%
elongation	elongation	Break	ASTM D412	360	%
tensile strength	Yield,23°C	ISO 37	5.86	MPa
Permanent compression deformation	70°C,22hr	ASTM D395B	76	%
	Permanent compression deformation	24°C,22hr	ASTM D395B	19	%
		Permanent compression deformation	100°C,22hr	ASTM D395B	87	%
			Permanent compression deformation	24°C,22hr	ISO 815	19	%
				Permanent compression deformation	70°C,22hr	ISO 815	76	%
				Permanent compression deformation	Permanent compression deformation	100°C,22hr	ISO 815	87	%
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Taber wear resistance	1000Cycles,1.0E+6g,CS-17Wheel	ASTM D1044	144	mg
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Brittle temperature		ASTM D746	-67.8	°C
Brittle temperature	Brittle temperature		ISO 812	-67.8	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD：1.59mm	ASTM D955	1.9	%
density		ISO 1183	1.06	g/cm³
density	density		ASTM D792	1.06	g/cm³
Shrinkage rate	MD:3.18mm	ISO 294-4	2.1	%
	Shrinkage rate	TD:3.18mm	ISO 294-4	0.40	%
		Shrinkage rate	MD：3.18mm	ASTM D955	2.1	%
			Shrinkage rate	TD：1.59mm	ASTM D955	0.0	%
				Shrinkage rate	TD：3.18mm	ASTM D955	0.40	%
					Shrinkage rate	TD:1.59mm	ISO 294-4	0.0	%
					Shrinkage rate	Shrinkage rate	MD:1.59mm	ISO 294-4	1.9	%
MeltViscosity	190°C,300sec^-1	ASTM D3835	327	Pa·s
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shore hardness	ShoreA,5Sec	ASTM D2240	52
Shore hardness	Shore hardness	ShoreA,5Sec	ISO 868	52
aging	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume change	70°C,168hr,inASTM#1Oil	ISO 1817	16	%
	Volume change	24°C,168hr,inReferenceFuelB	ISO 1817	47	%
		Volume change	70°C,168hr,inWater	ASTM D471	1.0	%
			Volume change	70°C,168hr,inIRM903Oil	ASTM D471	95	%
			Volume change	Volume change	70°C,168hr,inASTM#1Oil	ASTM D471	16	%
Change rate of tensile strength in air	70°C,168hr	ASTM D573	17	%
	Change rate of tensile strength in air	100%Strain,70°C,168hr	ASTM D573	1.0	%
		Change rate of tensile strength in air	100°C,168hr	ASTM D573	47	%
			Change rate of tensile strength in air	100%Strain,100°C,168hr	ASTM D573	-5.0	%
				Change rate of tensile strength in air	70°C,168hr	ISO 188	17	%
					Change rate of tensile strength in air	100%Strain70°C,168hr	ISO 188	1.0	%
						Change rate of tensile strength in air	100°C,168hr	ISO 188	47	%
						Change rate of tensile strength in air	Change rate of tensile strength in air	100%Strain100°C,168hr	ISO 188	-5.0	%
Change rate of ultimate elongation in air	70°C,168hr	ASTM D573	6.0	%
Change rate of ultimate elongation in air	Change rate of ultimate elongation in air	100°C,168hr	ASTM D573	16	%
Volume change	70°C,168hr,inIRM903Oil	ISO 1817	95	%
	Volume change	70°C,168hr,inWater	ISO 1817	1.0	%
	Volume change	Volume change	24°C,168hr,inReferenceFuelB	ASTM D471	47	%
Tensile stress change rate	100°C,168hr，Break	ISO 1817	16	%
Tensile stress change rate	Tensile stress change rate	70°C,168hr，Break	ISO 1817	6.0	%