کاربردهای معمول:	زمینه خودرو \| ابزار الکتریکی
ویژگی‌ها:	سختی بالا \| مقاومت در برابر پیری \| عمومی \| صبر

گواهی‌نامه‌ها

برگه داده فنی

impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	250	kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	23°C	ISO 180/1U	280	kJ/m²
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	3.00	J
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	2000	N
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	8.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	280	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	320	kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	9.0	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating	0.8mm	IEC 60695-11-10,-20	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	22	%
FMVSS flammability		FMVSS302	B
Atomization	F-value(refraction)	ISO 6452	90	%
Atomization	Atomization	G-value(condensate)	ISO 6452	3.5E-04	g
Burning rate	1.00mm	ISO 3795	20	mm/min
UL flame retardant rating	0.8mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	1.5mm	UL 94	HB
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus		ISO 527-2	3100	Mpa
tensile strength	Yield	ISO 527-2	71.0	Mpa
Tensile strain	Yield	ISO 527-2	17	%
Nominal tensile fracture strain		ISO 527-2	30	%
Tensile creep modulus	1hr	ISO 899-1	2800	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1600	Mpa
Bending modulus		ISO 178	3000	Mpa
bending strength	3.5%Strain	ISO 178	80.0	Mpa
Poisson's ratio		ISO 527	0.35
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	160	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	95.0	°C
Vicat softening temperature		ISO 306/B50	155	°C
Ball Pressure Test	165°C	IEC 60695-10-2	Pass
Melting temperature		ISO 11357-3	178	°C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1E-04	cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1E-04	cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	9E-05	cm/cm/°C
				Linear coefficient of thermal expansion	TD：AnnealingTemperature	ISO 11359-2	160	°C
					Linear coefficient of thermal expansion	TD：AnnealingTime-Optional	ISO 11359-2	30.0	min/mm
					Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	9E-08	m²/s
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
density		ISO 1183	1.42	g/cm³
melt mass-flow rate		ISO 1133	15	g/10min
Melt Volume Flow Rate (MVR)	190°C/2.16kg	ISO 1133	13.0	cm3/10min
Shrinkage rate	TD	ISO 294-4	1.9	%
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	2.0	%
Water absorption rate	Saturation,23°C,2.00mm	ISO 62	1.4	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.40	%
MediumDensity			1.19	g/cm³
ThermalConductivityofMelt			0.24	W/m/K
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Surface resistivity		IEC 60093	4E+14	ohms
Volume resistivity		IEC 60093	2E+14	ohms·cm
Dielectric strength		IEC 60243-1	44	KV/mm
Relative permittivity	100Hz	IEC 60250	3.80
Relative permittivity	Relative permittivity	1MHz	IEC 60250	3.80
Dissipation factor	100Hz	IEC 60250	9E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	5.5E-03
Compared to the anti leakage trace index		IEC 60112	PLC 0
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness	M-Sale	ISO 2039-2	92
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	120
Ball Pressure Test	H358/30	ISO 2039-1	192	Mpa
Supplementary Information	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Emission		VDA275	<8.00	mg/kg
EmissionofOrganicCompounds		VDA277	3.10	µgC/g

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.