برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | Saturation | ASTM D570 | 5.0 % |
| melt mass-flow rate | 280°C/2.16kg | ASTMD1238 | 27 g/10min |
| Shrinkage rate | MD | ASTM D955 | 0.80to1.1 % |
| Shrinkage rate | TD | ASTM D955 | 0.80to1.1 % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 5.0 % |
| GranuleHumidity | | 内部方法 | <0.15 % |
| density | | ASTMD792 | 1.36to1.38 g/cm³ |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R-Scale | ASTM D785 | 116 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.0mm | UL 94 | HB |
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Hot filament ignition temperature | 2.0mm | IEC 60695-2-13 | 650 °C |
| Limiting Oxygen Index | | ASTM D2863 | 26 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| bending strength | Break | ASTM D790 | 150 MPa |
| Tensile modulus | | ASTMD638 | 7200 MPa |
| tensile strength | Yield | ASTMD638 | 85.0 MPa |
| tensile strength | Break | ASTMD638 | 74.0 MPa |
| elongation | Break | ASTMD638 | 2.5 % |
| Flexural modulus | | ASTMD790 | 7000 MPa |
| bending strength | -- | ISO 178 | 150 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | -20°C | ISO 179 | 30 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 38 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTMD256 | 40 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| dielectric strength | 2.00mm | ASTM D149 | 24 kV/mm |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 1 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 2 |
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 4.5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTMD648 | 160 °C |
| Continuous use temperature | --3 | IEC 60216 | 80.0 °C |
| Continuous use temperature | --4 | IEC 60216 | 120 °C |
| vicat | | ISO 306/B50 | 235 °C |
| ball-indentation hardness | 165°C | VDE0470 | 通过 |
| melting temperature | | ASTMD211 | 256 °C |