VLDPE FG B0 VERSALIS ITALY
0
مقایسهبرگه داده فنی
| شرایط آزمون | روش آزمون | نتیجه آزمون | |
|---|---|---|---|
| elongation | MD:断裂,吹塑薄膜 | ISO 527-3 | 500 % |
| TD:断裂,吹塑薄膜 | ISO 527-3 | 800 % | |
| Dart impact | Blown Film | ISO 7765-1 | 250 g |
| Elmendorf tear strength | MD | ISO 6383-2 | 70.0 kN/m |
| TD | ISO 6383-2 | 110.0 kN/m | |
| brittle temperature | ASTM D746 | <-70.0 °C | |
| vicat | ISO 306/A | 88.0 °C | |
| melting temperature | 内部方法 | 120 °C | |
| gloss | 45°,吹塑薄膜 | ASTM D2457 | 65 |
| Haze ratio | Blown Film | ISO 14782 | 6.0 % |
| density | ISO 1183 | 0.911 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 0.90 g/10min |
| coefficient of friction | 与自身-动态,吹塑薄膜 | ISO 8295 | >0.50 |
| film thickness | 10to50µm | ||
| Tensile modulus | 1%正割,MD:吹塑薄膜 | ISO 527-3 | 90.0 MPa |
| 1%正割,TD:吹塑薄膜 | ISO 527-3 | 100 MPa | |
| tensile strength | MD:屈服,吹塑薄膜 | ISO 527-3 | 7.00 MPa |
| TD:屈服,吹塑薄膜 | ISO 527-3 | 7.00 MPa | |
| MD:断裂,吹塑薄膜 | ISO 527-3 | 40.0 MPa | |
| TD:断裂,吹塑薄膜 | ISO 527-3 | 32.0 MPa |